Effect of the Intergranular Carbide on the Mechanical Properties of 316L Open Cell Steel Foams

316 L steel foams are lightweight structures that are considered to replace bulk steel materials. It is thought that it can be used as armor material with its energy absorption feature. In this study, the steel foams were annealed at three different temperatures, 650, 850 and 1050 degrees, respectively . In microstructure, it was observed that carbide was produced in materials which were annealed at 650 ° C for 24 hours. It was seen that carbides were not formed at other temperatures. Mechanical properties, however, did not change in the small modifications of the microstructure. For this reason, it is not expected that 316L steel foams will have a change in performance at high temperatures and in the severe conditions.



Keywords
metal foams, carbide, mecahnical properties, microstructure



Kaynakça

Gelişmiş Arama


Duyurular

    Yayın Duyurusu

    Yayına kabul edilen makaleler ilgili sayının yayın tarihi beklenmeden DOI verilmekte ve atıf almasına yönelik "Erken Görünüm" seçeneği ile yayınlanmaktadır. 


    Makale Kabulü Sürmektedir

    Dergimizin 5 (2) sayısı için makale kabulü 30 Kasım 2019 tarihine kadar sürecektir. Makalelerinizi herhangi bir word şablonunda "Online Makale Gönder" linkinden gönderebilirsiniz. Kabul edilen makalelerin tasarım ve mizanpajı dergimizin sekreteryası tarafından yapılmaktadır.



Adres : http://www.jocrest.com
Telefon : Please contact mail first Faks : Lütfen öncelikle mail ile iletişime geçiniz
Eposta : sra.academic.publishing@gmail.com

Web Yazılım & Programlama Han Yazılım Bilişim Hizmetleri